| Mechanical Characteristics |
| Type |
Tensile Strength(N/mm2) |
Elongation(%) |
Yield Strength(N/mm2) |
| WB090 |
450 |
55 |
250 |
| WB092 |
300 |
55 |
250 |
| WB08G |
420 |
5 |
230 |
| WB09G |
450 |
10 |
250 |
|
| Physical Characteristics |
| Type |
Speciflc Gravity
(G/cm3) |
Linear Expansion20-300
0C10-6/0C |
Heat Conductivity 20
CW0/m.k |
Electric rate 20
Cm/onm.mm2 |
Elastic Modulus
KN/mm2 |
| WB090 |
8.9 |
18.2 |
60 |
6.5 |
115 |
| WB092 |
8.9 |
18.2 |
60 |
6.5 |
115 |
| WB08G |
7.8 |
22 |
70 |
7.8 |
108 |
| WB09G |
8.0 |
18.2 |
60 |
6.5 |
115 |
|
| Wear Characteristics |
| Type |
Max.Dynamic Load
(N/mm2) |
Max.Speed (no,oil)
(m/s) |
Max.Speed (oil)
(m/s) |
Use Temperature(Degrees Celsius)
Temp. |
| WB090 |
75 |
/ |
2.5 |
-80~+200 |
| WB092 |
60 |
/ |
2.5 |
-100~+200 |
| WB08G |
65 |
0.4 |
4 |
-100~+260 |
| WB09G |
65 |
0.2 |
4 |
-100~+260 |
|
| Bushes Hardness |
| Type |
Ltem |
Hardness |
| WB090
WB092 |
Standard |
90~120 |
| Speciald |
125~155 |
| WB08G |
Standard |
60~90 |
| WB09G |
Standard |
90~120 |
| WBB090 |
Standard |
70~100 |
|
| Bushes Material |
| Type |
Ltem |
Material |
|
| Composition(%) |
| CU |
SN |
Pb |
Zn |
P |
Other |
WB090
WB092 |
Standard |
CuSn6.5P |
Remainder |
6~7 |
— |
— |
0.1~0.25 |
≤0.1 |
| SpecialI |
CuSn8P |
Remainder |
7~9 |
— |
— |
0.01~0.35 |
≤0.2 |
| (SpecialII |
H68(CuZn31Si) |
66~70 |
— |
≤0.8 |
Remainder |
— |
≤0.5 |
| WB08G |
Standard |
CuSn10Pb10+Gr |
Remainder |
9~11 |
9~11 |
— |
— |
≤0.5 |
| WB09G |
Standard |
CuSn6.5P+Gr |
Remainder |
6~7 |
— |
— |
0.1~0.25 |
≤0.1 |
| Special |
CuSn8P+Gr |
Remainder |
7~9 |
— |
— |
0.01~0.35 |
≤0.2 |
|
| WB090 Oil indentation |
 |
| Type |
Thickness |
Oil Depth |
| WB090 |
1mm |
0.3~0.4mm |
| 1.5mm |
0.4~0.5mm |
| 2mm |
0.5~0.6mm |
| 2.5mm |
0.6~0.7mm |
WB09G
WB08G |
0.65mm |
0.15~0.3mm |
| 1mm |
0.3~0.4mm |
| 1.5mm |
0.4~0.5mm |
| 2mm |
0.4~0.5mm |
| 2.5mm |
0.4~0.5mm |
|